316/316L/316Ti لفائف الفولاذ المقاوم للصدأ
وصف
| يكتب | درجة | درجة | المكون الكيميائي٪ | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | آخر | |||
| الأوستنيتي | 201 | SUS201 | .150.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | .0.060 | .030.030 | - | .001.00 | - | .250.25 | - |
| 202 | SUS202 | .150.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | .0.060 | .030.030 | .001.00 | - | .250.25 | － | ||
| 301 | 1.431 | .150.15 | 16.00-18.00 | 6.00-8.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | .10.10 | - | |
| 304 | 1.4301 | .070.07 | 17.00-19.00 | 8.00-10.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | - | |
| 304 لتر | 1.4307 | .030.030 | 18.00-20.00 | 8.00-10.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | - | |
| 304 هـ | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | - | |
| 309 | 1.4828 | .20.20 | 22.00-24.00 | 12.00-15.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | - | |
| 309S | * | .0.08 | 22.00-24.00 | 12.00-15.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | - | |
| 310 | 1.4842 | .250.25 | 24.00-26.00 | 19.00-22.00 | .002.00 | .00.045 | .030.030 | - | .51.50 | - | - | - | |
| 310S | * | .0.08 | 24.00-26.00 | 19.00-22.00 | .002.00 | .00.045 | .030.030 | - | .51.50 | - | - | - | |
| 314 | 1.4841 | .250.25 | 23.00-26.00 | 19.00-22.00 | .002.00 | .00.045 | .030.030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | .0.08 | 16.00-18.50 | 10.00-14.00 | .002.00 | .00.045 | .030.030 | 2.00-3.00 | .001.00 | - | - | - | |
| 316 لتر | 1.4404 | .030.030 | 16.00-18.00 | 10.00-14.00 | .002.00 | .00.045 | .030.030 | 2.00-3.00 | .001.00 | - | - | - | |
| 316 تي | 1.4571 | .0.08 | 16.00-18.00 | 10.00-14.00 | .002.00 | .00.045 | .030.030 | 2.00-3.00 | .001.00 | - | 0.1 | Ti5(C+N)~0.70 | |
| 317 | * | .0.08 | 18.00-20.00 | 11.00-15.00 | .002.00 | .00.045 | .030.030 | 3.00-4.00 | .001.00 | - | 0.1 | - | |
| 317 لتر | 1.4438 | .030.03 | 18.00-20.00 | 11.00-15.00 | .002.00 | .00.045 | .030.030 | 3.00-4.00 | .001.00 | - | 0.1 | - | |
| 321 | 1.4541 | .0.08 | 17.00-19.00 | 9.00-12.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | Ti5(C+N)~0.70 | |
| 321 هـ | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | Ti5(C+N)~0.70 | |
| 347 | 1.455 | .0.08 | 17.00-19.00 | 9.00-12.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | ملحوظة:10*C%-1.10 | |
| 347 هـ | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | .002.00 | .00.045 | .030.030 | - | .001.00 | - | - | ملحوظة:10*C%-1.10 | |
| xm-19 | نيترونيك50 | .0.06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | .00.045 | .030.030 | 1.50-3.00 | .001.00 | - | 0.2-0.4 | ملحوظة: 0.10-0.30 فولت: 0.10-0.30 | |
| 904 لتر | N08904 | .0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | .00.045 | .035.035 | .001.00 | 0.1 | النحاس: 1.0-2.0 | |||
| دوبلكس | 2205 | S32205 | .030.03 | 22.0-23.0 | 4.5-6.5 | .002.00 | .030.030 | .020.020 | 3.0-3.5 | .001.00 | - | 0.14-0.20 | |
| 2507 | S32750 | .030.03 | 24.0-26.0 | 6.0-8.0 | .21.20 | .035.035 | .020.020 | 3.0-5.0 | .80.80 | 0.5 | 0.24-0.32 | ||
| * | S32760 | .030.03 | 24.0-26.0 | 6.0-8.0 | .001.00 | .030.030 | .00.010 | 3.0-4.0 | .001.00 | 0.5-1.00 | 0.2-0.3 | ||
| 2304 | S32304 | .030.03 | 21.5-24.5 | 3.0-5.5 | .52.50 | .00.040 | .030.030 | 0.05-0.6 | .001.00 | 0.05-0.6 | 0.05-0.2 | ||
| 329 | 1.446 | .0.08 | 23.00-28.00 | 2.00-5.00 | .001.00 | .00.040 | .030.030 | 1.00-2.00 | .750.75 | - | - | ||
| الفريت | 409 | S40900 | .030.03 | 10.50-11.70 | 0.5 | .001.00 | .00.040 | .020.020 | - | .001.00 | - | .030.030 | Ti6(C+N)~0.50 ملحوظة:0.17 |
| 430 | 1Cr17 | .120.12 | 16.00-18.00 | - | .01.0 | .00.040 | .030.030 | - | .01.0 | - | - | - | |
| 444 | S44400 | .00.025 | 17.50-19.50 | 1 | .001.00 | .00.040 | .030.030 | 1.75-2.5 | .001.00 | - | 0.035 | تي + ملحوظة: 0.2 + 4 (C + N) ~ 0.80 | |
| 446 | S44600 | .20.20 | 23.00-27.00 | 0.75 | .51.5 | .00.040 | .030.030 | 1.50-2.50 | .001.00 | - | .250.25 | - | |
| مارتنسيت | 410 | 1Cr13 | 0.08-0.15 | 11.50-13.50 | 0.75 | .001.00 | .00.040 | .030.030 | - | .001.00 | - | - | - |
| 410S | * | .0.080 | 11.50-13.50 | 0.6 | .001.00 | .00.040 | .030.030 | - | .001.00 | - | - | - | |
| 416 | Y1Cr13 | .150.15 | 12.00-14.00 | 3) | .251.25 | .0.060 | ≥0.15 | - | .001.00 | - | - | - | |
| 420 | 2Cr13 | ≥0.15 | 12.00-14.00 | - | .001.00 | .00.040 | .030.030 | - | .001.00 | - | - | - | |
| 420J2 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | - | .001.00 | .00.040 | .030.030 | - | .001.00 | - | - | - | |
| 431 | 1Cr17Ni2 | .20.20 | 15.00-17.00 | 1.50-2.50 | .001.00 | .00.040 | .030.030 | - | .80.80 | - | - | - | |
| 440 درجة مئوية | 11Cr17 | 0.95-1.20 | 16.00-18.00 | - | .001.00 | .00.040 | .030.030 | 0.75 | .001.00 | - | - | - | |
| PH | 630 | 17-4PH | .070.07 | 15.00-17.50 | 3.00-5.00 | .001.00 | .035.035 | .030.030 | - | .001.00 | 3.00-5.00 | - | ملحوظة: 0.15-0.45 |
| 631 | 17-7PH | .0.09 | 16.00-18.00 | 6.50-7.50 | .001.00 | .035.035 | .030.030 | - | .001.00 | .50.50 | - | آل 0.75-1.50 | |
| 632 | 15-5PH | .0.09 | 14.00-16.00 | 3.50-5.50 | .001.00 | .00.040 | .030.030 | 2.00-3.00 | .001.00 | 2.5-4.5 | - | آل 0.75-1.50 | |
صفائح الفولاذ المقاوم للصدأ الصف توريد Baogu
| صقل الأسطح | الخصائص والتطبيق |
| 2B | سطوع السطح واستوائه رقم 2B أفضل من رقم no2D.ثم من خلال معالجة سطحية خاصة لتحسين خصائصه الميكانيكية، يمكن أن يلبي No2B الاستخدامات الشاملة تقريبًا. |
| رقم 1 | مصقول بحزام كاشطة من الحصى #100-#200، يتمتع بسطوع أفضل مع خطوط خشنة متقطعة، يستخدم كزخارف داخلية وخارجية للبناء والأجهزة الكهربائية وأدوات المطبخ وما إلى ذلك. |
| رقم 4 | مصقول بحزام جلخ من الحصى رقم 150-#180، يتمتع بسطوع أفضل مع خطوط خشنة متقطعة، ولكنه أرق من رقم 3، ويستخدم كمباني حوض الاستحمام والزخارف الداخلية والخارجية والأجهزة الكهربائية وأدوات المطبخ ومعدات تجهيز الأغذية وما إلى ذلك. |
| HL | مصقول بحزام كاشط من الحصى #150-#320 على النهاية رقم 4 وله خطوط مستمرة، يستخدم بشكل أساسي كمصاعد لزينة المباني، وأبواب المبنى، واللوحة الأمامية وما إلى ذلك. |
| BA | المدرفلة على البارد، الملدنة اللامعة والممررة بالجلد، المنتج يتمتع بسطوع ممتاز وانعكاس جيد مثل المرآة، وأجهزة المطبخ، والزخرفة وما إلى ذلك. |
| 8K | يتمتع المنتج بسطوع ممتاز ويفضل أن تكون المرآة انعكاسية. |